SABIC PC/PET X7300CL為低溫注塑成型PC，主要用于IMD、IML工藝
物性數據表：
| TYPICAL PROPERTIES (1) | ||||
| MECHANICAL | Value | Unit | Standard | |
| Tensile Stress, yld, Type I, 50 mm/min | 490 | kgf/cm2 | ASTM D 638 | |
| Tensile Stress, brk, Type I, 50 mm/min | 530 | kgf/cm2 | ASTM D 638 | |
| Tensile Strain, yld, Type I, 50 mm/min | 5 | % | ASTM D 638 | |
| Tensile Strain, brk, Type I, 50 mm/min | 150 | % | ASTM D 638 | |
| Tensile Modulus, 50 mm/min | 18700 | kgf/cm2 | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 840 | kgf/cm2 | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 19700 | kgf/cm2 | ASTM D 790 | |
| Tensile Stress, yield, 50 mm/min | 55 | MPa | ISO 527 | |
| Tensile Stress, break, 50 mm/min | 55 | MPa | ISO 527 | |
| Tensile Strain, yield, 50 mm/min | 5 | % | ISO 527 | |
| Tensile Strain, break, 50 mm/min | >150 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 1900 | MPa | ISO 527 | |
| Flexural Stress, break, 2 mm/min | 71 | MPa | ISO 178 | |
| Flexural Modulus, 2 mm/min | 2000 | MPa | ISO 178 | |
| IMPACT | Value | Unit | Standard | |
| Izod Impact, notched, 23°C | 67 | cm-kgf/cm | ASTM D 256 | |
| Instrumented Impact Total Energy, 23°C | 968 | cm-kgf | ASTM D 3763 | |
| Izod Impact, notched 80*10*4 +23°C | 9 | kJ/m2 | ISO 180/1A | |
| THERMAL | Value | Unit | Standard | |
| Vicat Softening Temp, Rate B/50 | 108 | °C | ASTM D 1525 | |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 102 | °C | ASTM D 648 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 88 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 1.15E-04 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 1.05E-04 | 1/°C | ASTM E 831 | |
| CTE, 23°C to 60°C, flow | 8.5E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 60°C, xflow | 8.5E-05 | 1/°C | ISO 11359-2 | |
| Vicat Softening Temp, Rate B/120 | 106 | °C | ISO 306 | |
| HDT/Ae, 1.8 MPa Edgew 120*10*4 sp=100mm | 90 | °C | ISO 75/Ae | |
| PHYSICAL | Value | Unit | Standard | |
| Specific Gravity | 1.2 | - | ASTM D 792 | |
| Mold Shrinkage, flow, 3.2 mm (5) | 0.4 - 0.8 | % | SABIC Method | |
| Mold Shrinkage, xflow, 3.2 mm (5) | 0.5 - 0.7 | % | SABIC Method | |
| Melt Flow Rate, 265°C/2.16kgf | 21 | g/10 min | ASTM D 1238 | |
| Density | 1.18 | g/cm3 | ISO 1183 | |
| Melt Volume Rate, MVR at 265°C/2.16 kg | 21 | cm3/10 min | ISO 1133 | |
| OPTICAL | Value | Unit | Standard | |
| Light Transmission, 2.54 mm | 88 | % | ASTM D 1003 | |
| Haze, 2.54 mm | 2 | % | ASTM D 1003 | |
注塑參數：
Parameter
Injection Molding Value Unit
Drying Temperature 80 - 95 °C
Drying Time 3 - 5 hrs
Drying Time (Cumulative) 8 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 250 - 270 °C
Nozzle Temperature 250 - 270 °C
Front - Zone 3 Temperature 250 - 270 °C
Middle - Zone 2 Temperature 245 - 265 °C
Rear - Zone 1 Temperature 240 - 250 °C
Mold Temperature 45 - 60 °C
Back Pressure 0.2 - 0.5 MPa
Screw Speed 20 - 100 rpm
Shot to Cylinder Size 40 - 80 %
Vent Depth 0.013 - 0.02 mm
具體信息，歡迎來電咨詢！
東積架新材料科技不僅是專業的熱塑性彈性體及工程材料原料供應商，，亦注重技術支持及全方位的解決方案，
提供從設計選材、模具設計、成型加工等系列幫助，亦可為客戶量身定制各特殊性能之材料，
進而協助客戶提高產品竟爭力!
歡迎來電咨詢！
東積架實業香港有限公司
EASTAR Industry (HK)Co.,Limited
深圳市東積架新材料科技有限公司
Shenzhen EASTAR New Materials Technology Co,.LTD
貴賓熱線：唐生13430746085
免責聲明：（1）以上所展示的信息由企業自行提供，內容的真實性、準確性和合法性由發布企業負責，環球塑化網對此不承擔任何保證責任。我們原則上建議您優先選擇“塑企通”會員合作! （2）同時我們鄭重提醒各位買/賣家，交易前請詳細核實對方身份，切勿隨意打款或發貨，謹防上當受騙。如發現虛假信息，請向環球塑化網舉報。
簡繁切換